Magnetic studies on one-step chemically synthesized nickel ferrite thin films

Authors
Lokhande, C. D.Kulkarni, S. S.Mane, R. S.Joo, Oh-ShimHan, Sung-Hwan
Issue Date
2011-12
Publisher
ELSEVIER SCI LTD
Citation
CERAMICS INTERNATIONAL, v.37, no.8, pp.3357 - 3360
Abstract
Nickel ferrite thin films were synthesized at room temperature using one-step electrodeposition solution processing. Reaction kinetics was also proposed. An effect of air baking on the structural, surface morphological and magnetic properties was investigated. As-deposited nickel ferrite thin films were cubic in crystal structure. Calculated grain size after annealing was increased from 30 to 48 nm in addition to formation of rough surface morphology. Due to decrease in defect levels after air baking the annealed nickel ferrite thin film showed saturation magnetization of 268 emu/cc, higher than non-annealed (230 emu/cc), when used in magnetic studies. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords
SEMICONDUCTING GAS SENSOR; DEPOSITION; ROUTE; IRON; SEMICONDUCTING GAS SENSOR; DEPOSITION; ROUTE; IRON; C. Magnetic properties; Electrosynthesis; Nickel ferrite; Thin films; Structural elucidation
ISSN
0272-8842
URI
https://pubs.kist.re.kr/handle/201004/129747
DOI
10.1016/j.ceramint.2011.05.136
Appears in Collections:
KIST Article > 2011
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE