Microstructural and optical properties of ZnO thin films grown on InSb(111) substrates
Authors
김태환D.U. LeeD.C ChooJ.H. leeM. JungJ. ChoK.Y. Seo윤영수
Keywords
thin film; optical properties
Issue Date
2001-07
Publisher
The Journal of physics and chemistry of solids
Citation
VOL 62, NO 7, 1199-1203
Abstract
ZnO thin films were grown on InSb (111) substrates with the goal of producing high-quality ZnO films and ZnO/InSb heterostructures. Atomic force microscopy images showed that the root-mean-square average surface roughness of the ZnO film was 17.26 Å, and X-ray diffraction measurements showed that the ZnO films grown on the InSb (111) substrates were preferential orientation in the [0001] crystal direction. Auger electron spectroscopy and bright-field transmission electron microscopy measurements showed that the ZnO/InSb heterostructures had no significant intermixing problems and had relatively sharp interfaces. The temperature dependence of the photoluminescence spectra showed dominantly the bound excition peaks at low temperature and the free exciton emission band at high temperature. These results indicate that ZnO (0001) preferential orientation textural films grown on p-InSb (111) substrates at low temperature hold promise for potential high-speed optoelectronic devices based on InSb substrates.
URI
http://pubs.kist.re.kr/handle/201004/13996
ISSN
0022-3697
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE