Effects of thermal annealing a glass surface in air
- Effects of thermal annealing a glass surface in air
- 장홍규; 황보선영; Y.K. Choi; K. Jeong; 황정남; C.H. Wang; D.J. Choi; 이석
- Issue Date
- Journal of non-crystalline solids
- VOL 296, 182-187
- Glass slides were annealed at a temperature range of 300–600 °C for 30 min in air. We investigated the effects of thermal annealing treatments on the chemical composition, and surface roughness of the glass. Metallic sodium concentration at the glass surface was 2.2%, but sodium concentration at the annealed glass surface ranged from 4.3% to 5.5%. The sodium composition at the glass surface was greatly increased at an annealing temperature of 400 °C, but the sodium composition at the surface was gradually decreased at Ta500 °C. This phenomenon may be due to the volatility of the sodium atoms at the glass surface. However, carbon concentration at the glass surface was reduced from 49% at room temperature to 22% at annealing temperature (Ta) of 600 °C. Surface morphology of the glass was changed with annealing temperature. The root-mean-square surface roughness of the bare glass was 0.6 nm, but the roughness of the glass annealed at a temperature of 300, 400, 500, and 600 °C in air for 30 min was 1.0, 1.8, 2.0, 3.0 nm, respectively.
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.