ZrSi2-SiC composite obtained from mechanically activated ZrC + 3Si powders by pulsed current activated combustion synthesis
- ZrSi2-SiC composite obtained from mechanically activated ZrC + 3Si powders by pulsed current activated combustion synthesis
- 고인용; 박정환; 윤진국; 남기석; 손인진
- Sintering; Nanocomposite; Mechanical properties; Solid state reaction
- Issue Date
- Ceramics international
- VOL 36, 817-820
- Dense nanostructured ZrSi2–SiC composite was simultaneously synthesized and consolidated by pulsed current activated combustion synthesis (PCACS) within 2 min in one step from mechanically activated powders of ZrC and 3Si. Highly dense ZrSi2–SiC with relative density of up to 97% was produced under simultaneous application of a pressure of 60 MPa and the pulsed current. The average grain size and mechanical properties of the composite were investigated.
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.