Suppression of Ni Agglomeration in PLD Fabricated Ni-YSZ Composite for Surface Modification of SOFC Anode
- Suppression of Ni Agglomeration in PLD Fabricated Ni-YSZ Composite for Surface Modification of SOFC Anode
- 노호성; 손지원; 이헌; 지호일; 이종호; 이해원
- SOFC; Nano-Structure Anode; PLD; Films; Microstructure-final; Nano-composites; ZrO2; Fuel cells
- Issue Date
- Journal of the European Ceramic Society
- VOL 30, NO 16, 3415-3423
- The suppression of Ni agglomeration in Ni-yttria stabilized zirconia (Ni-YSZ) nano-composite thin films deposited by pulsed laser deposition (PLD) has been investigated by varying post-annealing temperatures at a range of 800–1200 °C. Grain growth to a certain extent appears to be necessary to obtain a stable Ni-YSZ composite microstructure by suppressing massive Ni agglomeration. The microstructurally stable and uniform nano-porous Ni-YSZ thin film was obtained by 1200 °C post-annealing and reduction of the NiO–YSZ thin film, and it was applied as the surface modification layer of the bulk anode support used in conventional solid oxide fuel cells (SOFCs). By this approach, we were able to successfully realize a thin film electrolyte SOFC exhibiting the open cell voltage (OCV) higher than 1 V with a 1-μm thick film electrolyte on the porous anode support.
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.