Effects of Storage Condition on Degradation of Automotive Polymer Electrolyte Membrane Fuel Cells

Title
Effects of Storage Condition on Degradation of Automotive Polymer Electrolyte Membrane Fuel Cells
Authors
조은애
Keywords
PEMFC; Durability; MEA; Startup/shutdown; Degradation; Oxygen concentration
Issue Date
2010-11
Publisher
한국전기화학회지; Journal of the Korean Electrochemical Society
Citation
VOL 13, NO 4, 277-282
Abstract
Durability of automotive polymer electrolyte membrane fuel cell (PEMFC) strongly depends the startup/shutdown procedure. Formation of hydrogen/air boundary in the anode gas channel, so-called reverse current condition, particularly induces fast degradation of the cathode. Under the reverse current condition, high voltage is present at the cathode facing air in the anode gas channel and is a function of residual oxygen concentration in the gas channels, that increases with storage time and reaches 21% (air) eventually. In this study, effects of residual oxygen concentration in a PEMFC on degradation of the PEMFC. 자동차용 고분자전해질 연료전지의 열화는 시동 또는 정지 시에 ‘reverse-current condition’이라 불리는 현상에 의해 촉진된다. 연료전지 자동차의 운전 종료 후 장시간동안 주차를 해 두면, 대기 중의 공기가 스택 내로 서서히 유입되어 시간이 경과함에 따라 산소 분압이 점차 높아져 궁극적으로는 연료극과 공기극의 유로가 모두 공기로 충진된다. 이때 재시동하면서 연료극으로 수소가 공급되면, 연료극 유로 내에 수소와 공기가 공존하게 되고, 연료극에 공기가 존재하는 부위의 공기극에 1.4 V 이상의 높은 전압이 발생하는데, 이를 reverse-current condition 이라고 하며 공기극의 탄소 담지체와 백금 촉매 산화의 원인으로 작용한다. 본 연구에서는 재시동시 스택 내에 존재하는 산소의 농도에 따른 열화 현상을 규명하고자 하였다.
URI
http://pubs.kist.re.kr/handle/201004/38119
ISSN
1229-1935
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE