Sulfuric acid decomposition on Pt/SiC-coated-alumina catalysts for SI cycle hydrogen production

Title
Sulfuric acid decomposition on Pt/SiC-coated-alumina catalysts for SI cycle hydrogen production
Authors
정광덕정헌이승용김원주설용건
Keywords
Thermochemical hydrogen production; SI cycle; sulfuric acid decomposition; SiC coated catalyst
Issue Date
2013-05
Publisher
International journal of hydrogen energy
Citation
VOL 38, NO 14, 6205-6209
Abstract
Sulfuric acid decomposition was conducted at atmospheric pressure and a GHSV of 72,000 mL/gcat h in the temperature ranges from 650 to 850 °C. The Pt–Al (1wt% Pt/Al2O3) and and Pt–SiC–Al (1wt% Pt/SiC-coated-Al2O3) catalysts were prepared by an impregnation method. The Pt–Al catalyst rapidly deactivated at 650 and 700 °C, but was stable at 750 and 850 °C. The aluminum sulfate was observed on the spent Pt–Al catalyst by an FT-IR, an X-ray spectroscopy and a TGA/DSC analyzer, which was suggested to be a cause of the deactivation at lower reaction temperature. The alumina support was coated with SiC by a CVD method with methyltrichlorosilane (MTS) to get a non-corrosive support (SiC–Al) with high surface areas. The thermal analysis of the spent Pt–SiC–Al showed that the aluminum sulfate formation was suppressed during the sulfuric acid decomposition. The Pt–SiC–Al catalyst was not only active higher than the Pt–Al catalyst, but was also stable at all the tested reaction temperature.
URI
http://pubs.kist.re.kr/handle/201004/46479
ISSN
03603199
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE