Dehydrogenation of alkane to light olefin over PtSn/θ-Al2O3 catalyst: Effects of Sn loading

Title
Dehydrogenation of alkane to light olefin over PtSn/θ-Al2O3 catalyst: Effects of Sn loading
Authors
이미현Bhari Mallanna Nagaraja이관영정광덕
Keywords
alkane; potassium effect; PtSn alloy; dehydrogenation; Light olefin; Dehydrogenation of linear alkane; Effects of Sn
Issue Date
2014-09
Publisher
Catalysis today
Citation
VOL 232, 53-62
Abstract
Pt0.5Snx.x/θ-Al2O3 catalysts with different amount of tin (0.5, 0.75, 1.0 and 1.5 wt%) were prepared by a co-impregnation method. Propane dehydrogenation was performed at 873 K and a GHSV of 53,000 mL/(gcat h). The Pt0.5/θ-Al2O3 catalyst showed severe deactivation in alkane dehydrogenation reaction. The Sn addition decreased the cracking products of C1–C2 and the Pt0.5Sn0.75 catalyst with the highest Pt dispersion showed the highest C3 yield and C3 selectivity. n-Butane dehydrogenation was performed at 823 K and a GHSV of 18,000 mL/(gcat h). Similarly to propane dehydrogenation, the Sn addition to the Pt0.5/θ-Al2O3 catalyst decreased the cracking products of C1–C3. However, the Pt0.5Sn1.0 showed the highest n-C4 yield and the catalyst was steadily deactivated even at 823 K differently from propane dehydrogenation at 873 K. The small amount of Sn addition improved the C3 and n-C4 selectivity by blocking the cracking sites of Pt catalyst. The PtSn alloy formed after the reduction at 500 °C. The PtSn formation can enhance the C3 and n-C4 selectivity. The Pt dispersion on the Pt0.5/θ-Al2O3 catalyst increased with the Sn addition up to 0.75 wt%. The highest Pt metal dispersion was observed on the Pt0.5Sn0.75 catalyst. The conclusion was given to the Sn effects on the increase of Pt dispersion to enhance the activity as well as on the electronic and geometric effect of PtSn alloy to increase the stability and olefin selectivity.
URI
http://pubs.kist.re.kr/handle/201004/47743
ISSN
09205861
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE