Improved Tensile Strength and Thermal Stability of Thermoplastic Carbon Fiber Fabric Composites by Heat Induced Crystallization of In Situ Polymerizable Cyclic Butylene Terephthalate Oligomers

Title
Improved Tensile Strength and Thermal Stability of Thermoplastic Carbon Fiber Fabric Composites by Heat Induced Crystallization of In Situ Polymerizable Cyclic Butylene Terephthalate Oligomers
Authors
김성호노예지고영웅김성륜윤재륜
Keywords
탄소섬유복합소재; CFRP; 탄소섬유; Carbon fiber; 저점도 열가소성 수지; Cyclic butylene terephthalate; 열처리; Anealing
Issue Date
2014-09
Publisher
Polymer Engineering and Science
Citation
VOL 54, NO 9, 2161-2169
Abstract
Thermoplastic carbon fiber fabric reinforced composites (CFFRCs) were prepared using a novel fast manufacturing process with a low viscosity polymerizable cyclic butylene terephthalate (CBT) resin. Structure and properties of the composites altered by thermal annealing were investigated to develop appropriate post processing of the CFFRCs for fast production and lowering the processing cost. Annealing at 200°C for 120 min resulted in improved mechanical properties and thermal stability of the polymerized CBT (pCBT) based on differential scanning calorimetry, wide-angle X-ray diffraction, and thermo gravimetric analysis. The tensile strength of the CFFRC compression molded at 250°C for 2 min was 440 MPa and that of the CFFRC annealed at 200°C for 120 min after compression molding was 500 MPa, which is an improvement of 550 and 625% relative to the pCBT matrix, respectively. In addition, the thermal stability of the CFFRC annealed at 250°C for 120 min improved by 10°C. Therefore, tensile strength and thermal stability of the manufactured CFFRC can be improved by using the appropriate annealing conditions.
URI
http://pubs.kist.re.kr/handle/201004/48005
ISSN
00323888
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE