Spectral-converting study of La1-m-nErmYbnOCl (m=0.001-0.2,
- Spectral-converting study of La1-m-nErmYbnOCl (m=0.001-0.2,
- 박상문; 조소혜
- 파장변환; 형광체; LaOCl; Er3+; Yb3+; Luminescence; Conversion; Energy transfer
- Issue Date
- Journal of luminescence
- VOL 153, 90-95
- Optical materials composed of La1−m−nErmYbnOCl (m=0.001–0.2, n=0–0.1) solid solution were prepared via a solid-state reaction using excess NH4Cl flux at 950 °C for 30 min. X-ray diffraction patterns of La1−mErmOCl were compared upon altering the molar ratios of the flux to the La3+ (Er3+, Yb3+) ions. By means of photoluminescence spectra, the dependence of the luminescence intensity as a function of the Er3+ content and the color CIE coordinates of the Er3+-doped layered LaOCl compounds were also investigated under excitation by near-ultraviolet (NUV) and visible light. The spectral conversion properties of Er3+ and Er3+–Yb3+ ions doped into LaOCl phosphors were elucidated under diode-laser irradiation of 980 nm in wavelength. The desired up-conversion of the emitting light, passing throughout the green, orange, and red regions of the spectrum, was achieved by appropriate Er3+ and/or Yb3+ concentrations in the LaOCl host structure under 980-nm-excitation light, while its mechanism in the phosphors was described by an energy-level schematic. Up-conversion emission spectra and the dependence of the emission intensity on pump power in the La0.89Er0.1Yb0.01OCl phosphor were investigated under diode-laser irradiation of both wavelengths, 980 and 1550 nm.
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.