Tunable luminescence in Bi3+ and Eu3+ co-doped Sr3AlO4F Oxyfluorides Phosphors
- Tunable luminescence in Bi3+ and Eu3+ co-doped Sr3AlO4F Oxyfluorides Phosphors
- 노민희; 조소혜; 박상문
- photoluminescence; oxyfluoride; Bi; Eu; phosphor
- Issue Date
- Journal of luminescence
- VOL 게재예정, 게재예정
- Luminescent materials composed of Sr3-3(m+n)/2BimEunAlO4F (m = 0.001–0.05, n = 0–0.1) were prepared by the solid-state reaction method. The excitation and emission spectra of Sr3-
3m/2BimAlO4F (m = 0.001–0.05) were investigated using photoluminescence spectroscopy; broadband emission peaks owing to the 3P1 1S0 transitions of the Bi3+ activator were observed centered near 427 nm. Critical emission quenching, as a function of Bi3+ content in Sr3-3m/2BimAlO4F, was observed at relatively low concentrations of the activator. The quantum efficiency of Sr2.985Bi0.01AlO4F in comparison with sodium salicylate was explored. When Sr2+ ions in the oxyfluoride host were replaced by Bi3+ and Eu3+ ions, the effective s2-sp and f-f transitions of the Bi3+ and Eu3+ ions, respectively, were simultaneously observed. The diverse excitation and emission photoluminescence spectra and color CIE coordinates, as well as the blue to orange-red emission, obtained using Sr3-3(m+n)/2BimEunAlO4F (m = 0–0.05, n = 0–0.1) phosphors are also discussed.
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.