Tetrazole substituted polymers for high temperature polymer electrolyte fuel cells

Title
Tetrazole substituted polymers for high temperature polymer electrolyte fuel cells
Authors
헨켄스마이어디억Duong Ngoc My HanhMateusz BrelaKarol DyduchArtur MichalakKatja Jankova조형래장종현김형준Lars N. CleemannQingfeng LiJens Oluf Jensen
Keywords
HT PEMFC; PA doping; tetrazole; membrane; DFT
Issue Date
2015-07
Publisher
Journal of materials chemistry. A, Materials for energy and sustainability
Citation
VOL 3, NO 27, 14389-14400
Abstract
While tetrazole (TZ) has much lower basicity than imidazole and may not be fully protonated in the presence of phosphoric acid (PA), DFT calculations suggest that the basicity of TZ groups can be increased by the introduction of a 2,6-dioxy-phenyl-group in position 5 of TZ. This structure allows hydrogen bonds between TZ protons and ether oxygen atoms, and thereby establishes a resonance stabilised, co-planar structure for tetrazolium ions. Molecular electrostatic potential (MEP) calculations also indicate that tetrazolium ions possess two sites for proton hopping. This makes such materials interesting for use in a high temperature fuel cell (HT PEMFC). Based on these findings, two polymers incorporating the proposed TZ groups were synthesised, formed into membranes, doped with PA and tested for fuel cell relevant properties. At room temperature, TZ-PEEN and commercial meta-PBI showed an equilibrium uptake of 0.5 and 4.7 mol PA per mol heterocycle, respectively, indicating that PBI has higher affinity for PA than TZ-PEEN. The highest achieved PA uptake was ca. 110 wt%, resulting in a proton conductivity of 25 mS cm 1 at 160 C with a low activation energy of about 35 kJ mol 1. In a first HT PEMFC test at 160 C, a peak power density of 287 mW cm 2 was achieved.
URI
http://pubs.kist.re.kr/handle/201004/49953
ISSN
20507488
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE