Nitrogen-doped Carbon Coated Porous Silicon as High Performance Anode Material for Lithium-Ion Batteries

Title
Nitrogen-doped Carbon Coated Porous Silicon as High Performance Anode Material for Lithium-Ion Batteries
Authors
이중기정경윤최원창정훈기정민기모비눌이윤성두 호앙 롱선호현
Keywords
Silicon; Anode; Nitrogen-doped carbon; Lithium-ion battery
Issue Date
2016-08
Publisher
Electrochimica acta
Citation
VOL 209, 299-307
Abstract
An effective approach to generate nitrogen-doped carbon coating layer on porous silicon (CN@P-Si), one of most promising anode materials for lithium-ion batteries, was addressed in this study to minimize their intrinsic drawbacks of low electrical conductivity and large volume expansion. The resulting enhanced electrochemical performance of the cell using the prepared CN@P-Si materials is attributed to the suppression of volume expansion and formation of the stable solid electrolyte interface by the combination of the porous structure and nitrogen-doped carbon coating layer during the repeated lithiation and delithiation process. After 100 cycles at 0.8 A g− 1, the capacity retention is 82% in contrast to 69% for the non-coated samples. Even at the increased discharge current of 20 A g− 1, the cell with CN@P-Si electrode delivers a high specific capacity of 1904 mAh g− 1. After 100 cycles, the P-Si electrode with pores shows huge pulverization; in contrast the CN@P-Si electrode remains intact with reasonably low volume expansion. Nitrogen-doped carbon coating layer on porous Si surface successfully suppress the pulverization of CN@P-Si electrode owing to its shielding capability. These results suggest that CN@P-Si is an attractive candidate for a high-capacity anode for lithium-ion batteries.
URI
http://pubs.kist.re.kr/handle/201004/59316
ISSN
00134686
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE