Synthesis of Sr2Nb3O10 nanosheets and their application for growth of thin film using an electrophoretic method

Title
Synthesis of Sr2Nb3O10 nanosheets and their application for growth of thin film using an electrophoretic method
Authors
최지원Woong-Hee LeeMir ImSang-Hyo KweonJong-Un WooSahn NahmSeong-Ju Hwang
Keywords
dielectric materials/properties; electrophoretic deposition; layered ceramics; thin films
Issue Date
2017-03
Publisher
Journal of the American Ceramic Society
Citation
VOL 100, NO 3-1107
Abstract
K(Sr2Nb3)O10 (KSN) ceramic without the secondary phase was obtained from a KSN + 0.05K2O specimen sintered at 1350°C. This ceramic was used as the precursor to synthesize Sr2Nb3O10− (SNO− ) nanosheets, because it has a pure KSN phase with a large (002) plane. The SNO− nanosheets were deposited on a Pt/Ti/SiO2/Si substrate using the electrophoresis method at room temperature, and heated at various temperatures to get rid of the organic defects. The crystalline SNO phase without organic defects was formed in film annealed at 600°C. However, when the annealing temperature exceeded 600°C, the Pt electrode became unstable, resulting in degradation of the SNO film. Good electric properties were obtained from the SNO film annealed at 600°C: dielectric constant of 70, dielectric loss of 0.017 at 1.0 MHz, leakage current density of 3.5×10− 8 A/cm2 at 0.2 MV/cm, and a breakdown electric field of 0.25 MV/cm.
URI
http://pubs.kist.re.kr/handle/201004/65864
ISSN
0002-7820
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE