The role of Fe particle size and oxide distribution on the hydrogenation properties of ball-milled nano-crystalline powder mixtures of Fe and Mg

Title
The role of Fe particle size and oxide distribution on the hydrogenation properties of ball-milled nano-crystalline powder mixtures of Fe and Mg
Authors
조영환서진유심재혁이영수줄리앙 파도누보정지윤Eric Fleury
Issue Date
2019-10
Publisher
Journal of alloys and compounds
Citation
VOL 806-1046
Abstract
In the aim of evidencing the relationship between Mg2FeH6 synthesis and the size of Fe particles, several specimens have been prepared by applying various milling energies (milling time) on a 2.1  Mg and 1Fe powder mixture doped with a small fraction of Unsaturated Fatty Amine (UFA). The resulting nano-crystalline composite structures display a broad Fe particle size distribution as a function of milling time. The hydrogenation of those complex powders has been conducted at temperatures lower than 400  °C under 60  bar of hydrogen pressure. As expected, the Fe particle size significantly influenced the hydrogenation kinetics. Also, the inevitable distribution of a minor fraction of oxides occurring during the milling process affected greatly the hydrogen storage capacity. Under the low pressure and temperature conditions selected in the frame of this study, lower than 100  bar and 500  °C conventionally used for synthesis of high purity Mg2FeH6, the hydrogenation reaction was demonstrated to be almost completed within 6  h, confirming the fast hydrogen absorption capability of the prepared materials. Plus, nearly 84  wt% of Mg2FeH6 was achieved under the afore mentioned moderate conditions and a minor fraction of unreacted Fe still remained due to diffusion constraints existing at low temperatures.
URI
http://pubs.kist.re.kr/handle/201004/69703
ISSN
0925-8388
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE