Influence of support composition on enhancing the performance of Ce-V on TiO2 comprised tungsten-silica for NH3-SCR

Title
Influence of support composition on enhancing the performance of Ce-V on TiO2 comprised tungsten-silica for NH3-SCR
Authors
하헌필김종식권동욱이소민이관영
Issue Date
2021-01
Publisher
Catalysis today
Citation
VOL 359-123
Abstract
The roles of WO3 and SiO2 in Ce-V catalysts supported on TiO2 comprised tungsten-silica were investigated systematically for NH3-SCR (selective catalytic reduction) and NH3-oxidation at high temperatures. When SiO2 and WO3 were added to TiO2, the surface area of Ce-V/TWS was maximized and the formation of Tisingle bondOsingle bondSi bond reduced nanoparticle size compared to without SiO2. The Ce-V/TWS surface had greater abundance of catalytic defects and surface oxygen species via XPS results. Increasing the (V4+?+?V3+) fraction increased the catalytic activity, which is attributed to the enhanced SCR performance at a wide temperature range due to the addition of WO3 and SiO2 to TiO2. The catalysts using the TWS supports exhibit high catalytic activity, since WO3 and SiO2 can promote redox properties. It was shown that Ce-V/TWS was the most suitable catalyst for selectively producing N2 via thermodynamically unavoidable NH3 direct oxidation as the temperature increased. In addition, hydrothermal aging effects were investigated for the Ce-V/TWS catalyst prepared by TiO2 supports including WO3 and SiO2 (comparison with vanadium-tungsten/titania). This study demonstrates the feasibility of utilizing WO3 and SiO2 in the TiO2 support as a possible way to increase catalytic activity and N2 selectivity in NH3-SCR at high temperatures.
URI
http://pubs.kist.re.kr/handle/201004/72822
ISSN
0920-5861
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE