Effect of silver addition on formation of secondary phases in squeeze cast Al-Cu-Mg alloys

Title
Effect of silver addition on formation of secondary phases in squeeze cast Al-Cu-Mg alloys
Authors
김유찬김도향김원태한요섭이호인
Keywords
squeeze casting; Al-Cu-Mg alloy; Silver alloying; Microstructure
Issue Date
2001-02
Publisher
Materials science and technology : MST : a publication of the Institute of Metals
Citation
VOL 17, NO 2, 215-222
Abstract
The effect of silver addition on the formation of secondary phases in squeeze cast Al–4.0Cu–1.5Mg and Al–4.0Cu–1.5Mg–0.7Ag (all wt-%) alloys has been investigated using optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffractometry, and transmission electron microscopy. The as cast microstructure of both alloys consists of primary dendritic α-Al and various types of secondary solidification phase, e.g. Al2Cu, Al2CuMg, Al(Cu,Ag)Mg, and icosahedral (I) and decagonal (D) quasicrystalline phases. However, the solidification path in the interdendritic region during squeeze casting is different for each alloy, i.e. L→ternary α-Al–Al2Cu–Al2CuMg eutectic in Al–4.0Cu–1.5Mg and L→L′+Al2Cu→α-Al–Al2Cu–Al(Cu0.75Ag0.25)Mg eutectic in Al–4.0Cu–1.5Mg–0.7Ag. This indicates that silver acts as an alloying element stabilising the formation of Al(Cu,Ag)Mg Laves phase. The remaining copper and iron rich liquid in the interdendritic region at the final stage of solidification solidifies into a mixed structure of α-Al, Al2Cu, and AlCuFe I (or D) phases. The composition of the I and D phases, measured by energy dispersive X-ray spectroscopy, is in the range Al–(27∼28)Cu–(9∼10)Fe and Al–(26∼27)Cu–(7∼9)Fe (all at.-%) respectively.
URI
http://pubs.kist.re.kr/handle/201004/9523
ISSN
0267-0836
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE