Kim, Minsung Park, Jinseon Kim, Sang Hoon Lee, Jung-Hyun Jeong, Keunhong Kim, Jongsik 2024-01-19T10:30:43Z 2024-01-19T10:30:43Z 2023-02-10 2023-01 0008-6223 https://pubs.kist.re.kr/handle/201004/114130 Homolytic and heterolytic H2O2 scissions are central to produce center dot OH for aqueous contaminant fragmentation. However, the kinetic, mechanistic, and energetic aspects of homolytic H2O2 cleavage remain under-explored, providing impetus for research with the use of difficult-to-degrade phenol as a model pollutant. Herein, UiO-66 and its analogues functionalized with -NH2/-SO3H (UiO-66-NH2/UiO-66-SO3H) were synthesized to generate ZrO2 poly-crystallites on N/S-doped carbon catalysts via pyrolysis (CUiO-66/CUiO-66-NH2/CUiO-66-SO3H). The catalyst surfaces contained distinct concentrations of Lewis basic N/S dopants, which donated electrons to adjacent Bro center dot nsted acidic -OH (BA) and Lewis acidic Zr4+ (LA) species dissimilarly, resulting in the catalysts with diverse BA/LA strengths (EBA/ELA) and areas (SBA/SLA). CUiO-66 exhibited the highest ELA and lowest EBA, which are favorable for endothermic H2O2 distortion, whereas CUiO-66-SO3H exhibited the lowest ELA and highest EBA, with only EBA being favorable for endothermic center dot OH desorption, while leaving the other elementary steps exothermic. Kinetic analysis and DFT calculations revealed that CUiO-66-SO3H possessed the lowest energy barrier (EBARRIER), demonstrating center dot OH desorption was the rate-determining step alongside with the significance of high EBA for reducing EBARRIER. Meanwhile, the highest pre-factor was observed for CUiO-66 with the largest SLA, corroborating the significance of large SLA for escalating the collision frequency between Zr4+ and H2O2/center dot OH. These results boost to adjust EBA/SLA for promoting center dot OH productivity via catalytic H2O2 homolysis. English Pergamon Press Ltd. Metal-organic framework-derived ZrO2 on N/S-doped porous carbons for mechanistic and kinetic inspection of catalytic H2O2 homolysis Article 10.1016/j.carbon.2022.12.023 1 Carbon, v.203, pp.630 - 649 Carbon 203 630 649 N scie scopus 000904951400001 2-s2.0-85144605089 Chemistry, Physical Materials Science, Multidisciplinary Chemistry Materials Science Article HYDROGEN-PEROXIDE NITROGEN OXIDE OXIDATION SURFACE ADSORPTION UIO-66 DECOMPOSITION PERFORMANCE REACTIVITY Metal -organic framework Pyrolysis Non -reducible metal Dopant Br ?nsted Lewis acidity Homolytic H 2 O 2 scission