Mara, Ikhsan M. Saleem Abbas Xuan Huy Do Seung-Young Choi Kobra Azizi Hans Aage Hjuler Jong Hyun Jang Heung Yong Ha Dirk Henkensmeier 2024-01-19T12:03:41Z 2024-01-19T12:03:41Z 2022-02-17 2022-05 1385-8947 https://pubs.kist.re.kr/handle/201004/115269 Polybenzimidazole (PBI) has been considered as promising membrane material for all-vanadium redox flow batteries (VRFBs) due to its compact morphology that can hinder vanadium crossover. However, its 2？4 mS cm？1 proton conductivity remains a challenge to achieve high energy efficiency. Recently developed PBI membranes showed conductivity up to 18 mS cm？1 by pre-treatment with phosphoric acid (PA) and up to 56 mS cm？1 with KOH. However, since the operation of VRFB uses sulfuric acid (SA), pre-treatment with different chemicals generates chemical wastes. Here we investigate the effects of pre-treaments with SA at various concentrations and temperatures. The optimized membrane (25C_10M, pretreated at 25 °C in 10M SA) increases its thickness during the treatment from 10 to 17 ？m, and shows an improved conductivity in 2 M SA of 9.1 mS cm？1. In V4+ containing electrolyte, the area specific resistance was 262 mΩ cm2, which is 3.3 and 1.7 times better than for 10 ？m thick standard PBI (13 ？m thick in 2 M SA) and 54 ？m thick Nafion 212 membranes, respectively. The selectivity is 458x104 S min cm？3, 7, 30, and 29 times better than for PA, KOH pre-swelling, and Nafion 212 membranes, respectively. A VRFB performance test with a 17 ？m thick 25C_10M PBI membrane showed an energy efficiency of 89.6% at 80 mA cm？2. ？ 2022 The Author(s) English Elsevier BV Polybenzimidazole membranes for vanadium redox flow batteries: Effect of sulfuric acid doping conditions Article 10.1016/j.cej.2022.134902 1 Chemical Engineering Journal, v.435 Chemical Engineering Journal 435 Y scie scopus 000773616800001 2-s2.0-85123843547 Engineering, Environmental Engineering, Chemical Engineering Article ELECTROLYTE MEMBRANES PROTON CONDUCTIVITY EXCHANGE MEMBRANES SULFONATION DEGREE ION-TRANSPORT PERFORMANCE MECHANISM SELECTIVITY SCATTERING EFFICIENCY interchain spacing Polybenzimidazole Pre-treatment Redox flow battery Sulfuric acid