Lee, S. H. Byeon, J. W. Doh, J. M. Lim, H. N. Yoon, J. K. Jung, H. Y. 2024-01-19T13:39:04Z 2024-01-19T13:39:04Z 2022-03-07 2007 0255-5476 https://pubs.kist.re.kr/handle/201004/116439 Effects of 0.5 wt% Sn-addition to the dental casting Au-12Pt-0.6Cu alloy oil the interfacial microstructures and bonding strength between porcelain and the alloy were investigated. Porcelain powders (SiO2-based oxides) are bonded through a thermal schedule consisting of pre-oxidation, 1(st) firing, and 2(nd) firing. Interfacial microstructures were examined after pre-oxidation and 2(nd) firing, respectively, by scanning and transmission electron microscopy. The bonding strength of the Au-12Pt-0.6Cu and Au-12Pt-0.6Cu-0.5Sn alloys with porcelain was about 24.6 MPa and 46.2 MPa, respectively. The higher bonding strength of the Sn-added alloy compared with that of the alloy without Sri is attributed to the SnO2 formed at the interface between porcelain and the alloy during pre-oxidation. SnO2 layer is thought to enhance chemical bonding with various oxides in the porcelain and, accordingly, improve bonding strength. English TRANS TECH PUBLICATIONS LTD Effect of Sn-addition on the bonding strength between casting Au-Pt-Cu alloy and SiO2-based porcelain Conference 10.4028/www.scientific.net/MSF.544-545.175 1 8th International Symposium on Eco-Materials Processing and Design, v.544-545, pp.175 - + 8th International Symposium on Eco-Materials Processing and Design 544-545 175 + SZ Kitakyushu, JAPAN 2007-01-11 ECO-MATERIALS PROCESSING AND DESIGN VIII 000246224300044 2-s2.0-38349176950 Proceedings Paper