Kim, Jung Hyuk Kim, Bosung Kim, Sang-Woo Kang, Hyun Wook Park, Min-Chul Park, Dong Hee Ju, Byeong Kwon Choi, Won Kook 2024-01-19T15:01:54Z 2024-01-19T15:01:54Z 2021-09-04 2021-04-02 0957-4484 https://pubs.kist.re.kr/handle/201004/117149 Coaxial type piezoelectric energy generator (C-PEG) nanofiber was fabricated by a self-designed continuous electrospinning deposition system. Piezoelectric PVDF-TrFE nanofiber as an electroactive material was electrospun at a discharge voltage of 9-12 kV onto a simultaneously rotating and transverse moving Cu metal wire at an angular velocity of omega(g) = 60-120 RPM. The piezoelectric coefficient d(33) of the PVDF-TrFE nanofiber was approximately -20 pm V-1. The generated output voltage (V-G) increased according to the relationship exp(-alpha P) (alpha = 0.41- 0.57) as the pressure (P) increased from 30 to 500 kpa. The V-G values for ten and twenty pieces of C-PEG were V-G = 3.9 V and 9.5 V at P = 100 kpa, respectively, relatively high output voltages compared to previously reported values. The high V-G for the C-PEG stems from the fact that it can generate a fairly high V-G due to the increased number of voltage collection points compared to a conventional two-dimensional (2-dim) capacitor type of piezoelectric film or fiber device. C-PEG yarn was also fabricated via the dip-coating of a PDMS polymer solution, followed by winding with Ag-coated nylon fiber as an outer electrode. The current and power density of ten pieces of C-PEG yarn were correspondingly 22 nA cm(-2) and 8.6 mu W cm(-3) at V-G = 1.97 V, higher than previously reported values of 5.54 and 6 mu W cm(-3). The C-PEG yarn, which can generate high voltage compared to the conventional film/nanofiber mat type, is expected to be very useful as a wearable energy generator system. English IOP PUBLISHING LTD NANOWIRES HYBRID NANOGENERATOR FIBER TEXTILES SENSOR High-performance coaxial piezoelectric energy generator (C-PEG) yarn of Cu/PVDF-TrFE/PDMS/Nylon/Ag Article 10.1088/1361-6528/abd57e 1 NANOTECHNOLOGY, v.32, no.14 NANOTECHNOLOGY 32 14 scie scopus 000607311900001 2-s2.0-85100320545 Nanoscience & Nanotechnology Materials Science, Multidisciplinary Physics, Applied Science & Technology - Other Topics Materials Science Physics Article NANOWIRES HYBRID NANOGENERATOR FIBER TEXTILES SENSOR coaxial piezoelectric energy generator (C-PEG) PVDF-TrFE nanofibers in-plane array C-PEG yarn characteristic output voltage-pressure curve