Dell'Agli, G. Spiridigliozzi, L. Pansini, M. Accardo, G. Yoon, S. P. Frattini, D. 2024-01-19T21:32:51Z 2024-01-19T21:32:51Z 2021-09-05 2018-10-15 0272-8842 https://pubs.kist.re.kr/handle/201004/120787 Variously co-doped Samaria-20 mol% doped ceria (SDC20) nanopowders were synthesized through a combined co-precipitation/hydrothermal treatment method under different carbonate environments. Urea and ammonium carbonate were used as both precipitating and mineralizing agent. In all cases, the adopted powder composition was Ce0.8Sm0.16 x O-0.04(1.9-delta) where X was either Ca, Sr, Er or Pr and delta is 0 for trivalent cations (i.e. Er and Pr) or 0.02 for divalent cations (i.e. Ca and Sr). The effects of different synthesis parameters on powders morphology and crystalline phases have been pointed out. Differently synthesized powders underwent structural and morphological transformations during the hydrothermal treatment leading to different crystalline precursors for the desired co-doped ceria nanopowders, i.e. crystallized into the fluorite-like cubic structure after a calcination step at 700 degrees C for 1 h. The final properties of the calcined powders are strongly related to the corresponding parent powder features, consequently determining different sintering behaviours in the various pellets. In particular, except for Er/Sm co-doped ceria, all samples synthesized with ammonium carbonate as precipitating/mineralizing agent exhibited excellent sintering behaviour, with remarkable values of relative density (higher than 97% and up to 99.4%) and an almost ideal microstructure. Definitely, the present work gives several guidelines in terms of synthesis parameters and conditions to produce, with a relatively simple and cheap process, highly reactive co-doped ceria nanopowders with tuned properties and suitable as electrolytes for intermediate temperature solid oxide fuel cells (IT-SOFCs). English ELSEVIER SCI LTD OXIDE FUEL-CELLS SOLID ELECTROLYTES AMMONIUM CARBONATE COPRECIPITATION TEMPERATURE CONDUCTIVITY MICROSTRUCTURE NANOPOWDERS PRECURSORS Effect of the carbonate environment on morphology and sintering behaviour of variously co-doped (Ca, Sr, Er, Pr) Samarium-doped Ceria in co-precipitation/hydrothermal synthesis Article 10.1016/j.ceramint.2018.06.269 1 CERAMICS INTERNATIONAL, v.44, no.15, pp.17935 - 17944 CERAMICS INTERNATIONAL 44 15 17935 17944 scie scopus 000445993000045 2-s2.0-85049348521 Materials Science, Ceramics Materials Science Article OXIDE FUEL-CELLS SOLID ELECTROLYTES AMMONIUM CARBONATE COPRECIPITATION TEMPERATURE CONDUCTIVITY MICROSTRUCTURE NANOPOWDERS PRECURSORS Carbonate environment Co-doped ceria Hydrothermal treatment Nanopowders Sintering