Nam, Seungjin Kim, Moon J. Hwang, Jun Yeon Choi, Hyunjoo 2024-01-19T21:34:50Z 2024-01-19T21:34:50Z 2021-09-03 2018-09-25 0925-8388 https://pubs.kist.re.kr/handle/201004/120894 In this study, Al0.15CoCrCuFeNiTix-C (x = 0, 1, 2) high-entropy alloys (HEAs) were produced via powder metallurgy routes, and the microstructural evolution and mechanical properties of the alloys were investigated with respect to the alloys of Ti content. Cr-carbides were formed in the Ti-free alloy, whereas the Ti-containing alloys contained Ti-carbides instead of Cr-carbides because Ti has a higher affinity for C than it does for Cr. Sigma phases were also formed in the Al0.15CoCrCuFeNiTi2-C alloy. The formation of carbides and intermetallic compounds altered the composition and structure of the solid-solution phases. High-energy ball-milling led to the refinement of microstructures to the nanoscale, and the average grain size of the alloys decreased with increasing Ti content because of the grain-boundary pinning effect of TiC. As a result, the Al0.15CoCrCuFeNiTix-C (x = 0, 1, 2) alloys exhibited high strengths of 2047, 2199, and 2877 MPa, respectively. (C) 2018 Elsevier B.V. All rights reserved. English ELSEVIER SCIENCE SA MECHANICAL-PROPERTIES PHASE-FORMATION COMPRESSIVE PROPERTIES STRUCTURAL EVOLUTION TENSILE PROPERTIES THERMAL-STABILITY WEAR-RESISTANCE SOLID-SOLUTION MICROSTRUCTURE BEHAVIOR Strengthening of Al0.15CoCrCuFeNiTix-C (x=0, 1, 2) high-entropy alloys by grain refinement and using nanoscale carbides via powder metallurgical route Article 10.1016/j.jallcom.2018.05.180 1 JOURNAL OF ALLOYS AND COMPOUNDS, v.762, pp.29 - 37 JOURNAL OF ALLOYS AND COMPOUNDS 762 29 37 scie scopus 000436600000005 2-s2.0-85047257563 Chemistry, Physical Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering Chemistry Materials Science Metallurgy & Metallurgical Engineering Article MECHANICAL-PROPERTIES PHASE-FORMATION COMPRESSIVE PROPERTIES STRUCTURAL EVOLUTION TENSILE PROPERTIES THERMAL-STABILITY WEAR-RESISTANCE SOLID-SOLUTION MICROSTRUCTURE BEHAVIOR High-entropy alloys Powder metallurgy Microstructures Mechanical properties