Jung, Jiyoon Cho, Hye Jin Kim, Dongyoung Hwang, Seung Sang Won, Jongok 2024-01-19T22:32:37Z 2024-01-19T22:32:37Z 2022-01-25 2018-06 2365-6549 https://pubs.kist.re.kr/handle/201004/121276 We have developed a thermally cured, natural lacquer (urushi)-based adhesive, which has a reversible polymer (RP) additive that promotes degradability. The RP was prepared by thermally treating a hemiaminal dynamic covalent network (HDCN) organo-gel. The urushi was crosslinked polymer from the curing reaction of urushiol. The main component of the natural lacquer is urushiol, which is the mixture of catechol derivatives containing alkyl side chains. The catechol group has a high adhesiveness, and the long alkyl chains provide high mechanical strength and flexibility. The thermal curing reaction occurred mainly between unsaturated C=C groups in the side alkyl chains of urushiol, and the rate of the curing reaction increased at higher temperature. HDCN was prepared via a reaction between formaldehyde and poly(propylene glycol) bis(2-aminopropyl ether) in 1-methyl-2-pyrrolidinone. Hexahydrotriazine-like RP, which is reversible in strong acid solution, was formed after heat treatment. Urushi/RP adhesives were degradable, and the degradation was investigated by tensile strength measurements. The tensile strength increased with increased RP in the urushi/RP adhesives because RP has a higher tensile strength than urushi. The tensile strength of the urushi/RP adhesives decreased by more than one order of magnitude after the material was immersed in 0.5 M of H2SO4 for 6 h, and the degradability increased with increased RP content. English WILEY-V C H VERLAG GMBH Degradable Natural Lacquer (Urushi) Adhesives Using a Reversible Polymer Based on Hemiaminal Dynamic Covalent Networks Article 10.1002/slct.201800849 1 CHEMISTRYSELECT, v.3, no.23, pp.6665 - 6670 CHEMISTRYSELECT 3 23 6665 6670 N scie scopus 000435933100050 2-s2.0-85048938039 Chemistry, Multidisciplinary Chemistry Article ORIENTAL LACQUER LAC TREE FILMS SAP CHEMISTRY urushiol natural adhesives urushi degradability tensile strength