Marinkas, Angela Struzynska-Piron, Izabela Lee, Yona Lim, Ahyoun Park, Hyun S. Jang, Jong Hyun Kim, Hyoung-Juhn Kim, Jihyun Maljusch, Artjom Conradi, Oliver Henkensmeier, Dirk 2024-01-19T22:33:29Z 2024-01-19T22:33:29Z 2021-09-03 2018-06 0032-3861 https://pubs.kist.re.kr/handle/201004/121324 For development of anion exchange membrane (AEM) water electrolysis systems, a series of polymers was synthesised by reacting 2-mesityl-benzimidazole (BIM) and brominated poly-(2,6-dimethyl-1,4-phenylene oxide) (Br-PPO) in a Menshutkin reaction, and permethylating the attached BIM groups. The degree of bromination of Br-PPO can be easily monitored by IR spectroscopy: A correlation with the shift of the band around 1190 cm(-1) was found. The IEC values of the prepared materials ranged between 1.6 and 2.9 mmol OH- g(-1). Only materials with an IEC value of 1.9 (PPO24-BIM) reproducibly formed self-supporting membranes. This may be related to the degree of crystallinity, which decreased from 14 to 3% when the IEC increased from 1.6 to 3 mmol OH(-)g(-1). Materials with IEC values of 1.6 and 2.2 can form self-supporting membranes, but not reproducibly. PPO24-BIM showed a conductivity of 8 mS cm(-1) at room temperature, a thermal stability well above 200 degrees C, and mechanical properties similar to those of commercial FAA3-30 membranes. During water electrolysis, a current density of 300 mA cm(-2) at 1.8 V was obtained. At 80 degrees C in 1 M KOH, degradation of BIM and the PPO backbone were observed by IR spectroscopy and monitoring conductivity and weight loss. (C) 2018 Elsevier Ltd. All rights reserved. English ELSEVIER SCI LTD Anion-conductive membranes based on 2-mesityl-benzimidazolium functionalised poly(2,6-dimethyl-1,4-phenylene oxide) and their use in alkaline water electrolysis Article 10.1016/j.polymer.2018.05.008 1 POLYMER, v.145, pp.242 - 251 POLYMER 145 242 251 N scie scopus 000433147700025 2-s2.0-85046708788 Polymer Science Polymer Science Article ETHER-LINKED POLYBENZIMIDAZOLE EXCHANGE MEMBRANES FUEL-CELLS PBI-OO STABILITY POLYMER DEGRADATION IONENES CATIONS BLENDS Alkaline stability Anion exchange membrane 2-Mesityl-benzimidazole Poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) Alkaline electrolysis