Dell'Agli, G. Spiridigliozzi, L. Marocco, A. Accardo, G. Frattini, D. Kwon, Y. Yoon, S. P. 2024-01-20T00:30:31Z 2024-01-20T00:30:31Z 2021-09-03 2017-10-15 0272-8842 https://pubs.kist.re.kr/handle/201004/122165 Nanocrystalline Samarium (20 mol%)-doped ceria (SDC20) nanopowders were prepared using a combined co-precipitation/hydrothermal treatment synthesis route carried out at reduced temperature (120 degrees C). The amorphous precursor experiences some microstructural transformations during the hydrothermal treatment, and after 16 h a Samarium-Cerium hydroxide carbonate, characterized by a hexagonal crystalline lattice, spherical morphology and particles of about 100 nm in size, with a very low degree of agglomeration, is the only present phase in contrast to the initial amorphous state. After the calcination step, the powders which preserved this morphology are still characterized by the absence of hard agglomerates. As a consequence, these powders exhibited an excellent sintering behaviour with a microstructure characterized by regular, equiaxed and micrometric grain size. In fact, at 1500 degrees C a nearly perfect densified sample was obtained, but also at 1300 degrees C a very good sintering behaviour was observed. Finally, the electrochemical characterization carried out by EIS measurements showed a very good electrical behaviour with high ionic conductivity, i.e. at 800 degrees C 5.2.10(-2) S cm(-1) and 4.8.10(-2) S cm(-1) for pellets sintered at 1500 degrees C and 1300 degrees C respectively, making them suitable for IT-SOFCs. English ELSEVIER SCI LTD HYDROTHERMAL SYNTHESIS GD ELECTROLYTES MECHANISM ZIRCONIA BEHAVIOR SM Morphological and crystalline evolution of Sm-(20 mol%)-doped ceria nanopowders prepared by a combined co-precipitation/hydrothermal synthesis for solid oxide fuel cell applications Article 10.1016/j.ceramint.2017.06.169 1 CERAMICS INTERNATIONAL, v.43, no.15, pp.12799 - 12808 CERAMICS INTERNATIONAL 43 15 12799 12808 scie scopus 000408287900164 2-s2.0-85021312435 Materials Science, Ceramics Materials Science Article HYDROTHERMAL SYNTHESIS GD ELECTROLYTES MECHANISM ZIRCONIA BEHAVIOR SM Ceramic electrolyte Electrochemical impedance Fuel cells materials Hydrothermal treatment Sintering Sm-doped eerie