Kwon, Byeong Wan Hu, Shuozhen He, Qian Marin-Flores, Oscar G. Oh, Chang Hoon Yoon, Sung Pil Kim, Jinsoo Breit, Joe Scudiero, Louis Norton, M. Grant Ha, Su 2024-01-20T05:31:41Z 2024-01-20T05:31:41Z 2022-01-25 2015-12 0926-3373 https://pubs.kist.re.kr/handle/201004/124657 The present paper describes the fabrication of a bilayer structured solid oxide fuel cell (SOFC). Its anode consists of molybdenum dioxide (MoO2)-based internal micro-reformer in the form of a porous thin film deposited over conventional Ni/YSZ cermet. Cell performance was measured by directly feeding a mixture of n-dodecane and air at different O-2/C ratios to the anode at 750 degrees C. Our findings show that the bilayer structured SOFC operating at an O-2/C ratio of 0.64 led to the highest initial cell performance with an initial maximum power density >4.0 W cm(-2). At a constant voltage of 0.7V and O-2/C ratio of 0.64, the bilayer structured SOFC showed a gradual increase in power density output over the first 2 h, followed by a stable output of 3.6W cm(-2) for the next 10 h. The tested cell showed no indication of coking and phase transformation. When a conventional Ni-based SOFC without the internal micro-reformer was operated under similar conditions, its initial performance and long-term stability were found to be significantly lower than that of bilayer structured SOFC due to Ni oxidation under high O-2/C ratio or coking under the low O-2/C ratio. These results open up new opportunities for efficiently generating electrical power from various types of high energy density liquid fuels using SOFCs with an integrated MoO2 micro- reformer. (C) 2015 Elsevier B.V. All rights reserved. English Elsevier BV Nickel-based anode with microstructured molybdenum dioxide internal reformer for liquid hydrocarbon-fueled solid oxide fuel cells Article 10.1016/j.apcatb.2015.05.048 1 Applied Catalysis B: Environmental, v.179, pp.439 - 444 Applied Catalysis B: Environmental 179 439 444 N scie scopus 000359873800048 2-s2.0-84930959947 Chemistry, Physical Engineering, Environmental Engineering, Chemical Chemistry Engineering Article PARTIAL OXIDATION CATALYST Internal micro-reformer Solid oxide fuel cells Molybdenum dioxide n-dodecane O-2/C ratio