Nguyen Dien Kha Tu Choi, Jaeyoo Park, Chong Rae Kim, Heesuk 2024-01-20T05:33:35Z 2024-01-20T05:33:35Z 2021-09-03 2015-11-10 0897-4756 https://pubs.kist.re.kr/handle/201004/124759 To allow for the use of graphene in various nano-electronic applications, the methods for the large-scale production of graphene with controllable electrical properties need to be developed. Here, we report the results of a fundamental study on the remarkable conversion between n- and p-type reduced graphene oxide (rGO) with changes in the thermal annealing temperature. It was found that the charge carriers in rGO for temperatures of 300-450 degrees C and 800-1000 degrees C are electrons (n-type), whereas for temperatures of 450-800 degrees C, they are holes (p-type). This is because the individual oxygen functional groups present on rGO are determined by the annealing temperature. We found that the predominance of electron-withdrawing groups (i.e., carboxyl, carbonyl, and sp(3)-bonded hydroxyl, ether, and epoxide groups) resulted in p-type rGO, although that of electron-donating groups (sp(2)-bonded hydroxyl, ether and epoxide groups) lead to n-type rGO. In addition, as a proof of concept, a flexible thermoelectric device consisting of GO-700 and GO-1000 as p-type and n-type components, respectively, was fabricated. This device, which contained eight pairs of the two components, exhibited an output voltage of 4.1 mV and an output power of 41 nW for Delta T = 80 K. These results demonstrate that the carrier characteristics of rGO can be altered significantly by changing the functional groups present on it, thus allowing it to be used in various applications including flexible thermoelectrics. English AMER CHEMICAL SOC STRUCTURAL EVOLUTION REDUCTION PHOTOLUMINESCENCE OXYGEN Remarkable Conversion Between n- and p-Type Reduced Graphene Oxide on Varying the Thermal Annealing Temperature Article 10.1021/acs.chemmater.5b02999 1 CHEMISTRY OF MATERIALS, v.27, no.21, pp.7362 - 7369 CHEMISTRY OF MATERIALS 27 21 7362 7369 scie scopus 000364614600020 2-s2.0-84946888128 Chemistry, Physical Materials Science, Multidisciplinary Chemistry Materials Science Article STRUCTURAL EVOLUTION REDUCTION PHOTOLUMINESCENCE OXYGEN