Kim, Jong-Hyun Kim, Dae-Hyeon Seo, In-Tae Hur, Joon Lee, Ji-Hyun Kim, Bo-Yun Nahm, Sahn 2024-01-20T06:01:52Z 2024-01-20T06:01:52Z 2022-01-25 2015-10 0924-4247 https://pubs.kist.re.kr/handle/201004/124911 CuO assisted the densification of KNbO3 (KN) ceramics sintered at 960 degrees C through the formation of a CuO-related liquid phase. Most of the Cu2+ ions entered the Nb5+ sites of the KN ceramics and acted as a hardener. In addition, the CuO-added KN (CKN) ceramics exhibited a double polarization versus electric field (P-E) loop and a sprout-shaped strain versus electric field (S-E) loop. The formation of these was attributed to the presence of defect dipoles formed by acceptor ions (Cu2+) and oxygen vacancies. In fact, owing to the high orthorhombic-to-tetragonal transition temperature of the CKN ceramics, the double P-E and sprout-shaped S-E loops developed without an aging process. Furthermore, the 1.0 mol% CuO-added KN ceramic exhibited a very high Q(m) value of 3005 with a large unipolar strain of 0.15% at 8.0 kV/mm. (C) 2015 Elsevier B.V. All rights reserved. English ELSEVIER SCIENCE SA Effect of CuO on the ferroelectric and piezoelectric properties of lead-free KNbO3 ceramics Article 10.1016/j.sna.2015.08.015 1 SENSORS AND ACTUATORS A-PHYSICAL, v.234, pp.9 - 16 SENSORS AND ACTUATORS A-PHYSICAL 234 9 16 N scie scopus 000363826400002 2-s2.0-84940643426 Engineering, Electrical & Electronic Instruments & Instrumentation Engineering Instruments & Instrumentation Article CRYSTALS Lead-free piezoelectrics Double polarization versus electric field loop Sprout-shaped strain versus electric field loop Hardening effect