Mocherla, Pavana S. V. Gautam, Sanjeev Chae, Keun Hwa Rao, M. S. Ramachandra Sudakar, C. 2024-01-20T06:04:44Z 2024-01-20T06:04:44Z 2021-09-05 2015-09 2053-1591 https://pubs.kist.re.kr/handle/201004/125062 We demonstrate that oxygen vacancies (VO) produced by aliovalent (Ca2+) doping in BiFeO3 (BCFO) and associated structural changes due to V-O ordering result in systematic alteration of the bandgap (E-g) over a wide range from 1.5 eV to 2.3 eV. By contrast, the change in the bandgap of a Ca2+ and Ti4+ co-doped BiFeO3 (BCFTO) system, wherein the V-O formation is suppressed, is negligible. These contrastive results strongly confirm the role of oxygen vacancies in altering the bandgap of BCFO. Irrespective of doping, microstrain, which is found to be large (0.3 to 1.2%) below a critical size (d(c) similar to 60 nm) also produces a small, yet linear change in the bandgap (E-g from 2.0 to 2.3 eV). The cubic phase stabilizes gradually in BCFO for x > 0.1 through an orthorhombic phase (for 0.05 < x < 0.1), whereas it directly transforms for x > 0.1 in BCFTO. This change in BCFO at 300 K suggests a high-pressure-like (or high-temperature-like) effect of the oxygen vacancies and dopants on the structure. Systematic variations in the relative intensities and peak positions of Fe d-d transitions in BCFO reveal the local changes in Fe-O-Fe coordination. These results along with XANES and HRTEM studies substantiate the observed structural changes. English IOP PUBLISHING LTD X-RAY-ABSORPTION ELECTRONIC-STRUCTURE SOLAR-CELLS BIFEO3 TRANSITION GAP MULTIFERROICS OXIDES PHASE SIZE Wide-range tunable bandgap in Bi1-xCaxFe1-yTiyO3-delta nanoparticles via oxygen vacancy induced structural modulations at room temperature Article 10.1088/2053-1591/2/9/095012 1 MATERIALS RESEARCH EXPRESS, v.2, no.9 MATERIALS RESEARCH EXPRESS 2 9 scie scopus 000370057200012 2-s2.0-84953241411 Materials Science, Multidisciplinary Materials Science Article X-RAY-ABSORPTION ELECTRONIC-STRUCTURE SOLAR-CELLS BIFEO3 TRANSITION GAP MULTIFERROICS OXIDES PHASE SIZE bandgap engineering oxygen vacancies Fe d-d transitions XANES HRTEM