Kim, Dae-Hyeon Joung, Mi-Ri Seo, In-Tae Hur, Joon Kim, Jong-Hyun Kim, Bo-Yun Lee, Hwack-Joo Nahm, Sahn 2024-01-20T08:04:17Z 2024-01-20T08:04:17Z 2022-01-25 2014-12 0002-7820 https://pubs.kist.re.kr/handle/201004/126016 Dielectric and piezoelectric properties of CuO-added KNbO3 (KN) ceramics were investigated. The CuO reacted with the Nb2O5, formed a CuO-Nb2O5-related liquid phase during the sintering, and assisted the densification of the KN ceramics at low temperatures. Moreover, some of the Cu2+ ions replaced the Nb5+ ions in the matrix and behaved as a hardener. The dielectric and piezoelectric properties of the KN ceramics were considerably influenced by the relative density. The 1.0mol% CuO-added KN ceramic sintered at 960 degrees C for 1.0h, which showed a maximum relative density, exhibited a high phase angle of 86.9 degrees, P-r of 14.8C/cm(2), and E-c of 1.8kV/mm. This specimen also exhibited good dielectric and piezoelectric properties: epsilon(T)(33)/epsilon(o) of 364, d(33) of 122pC/N, k(p) of 0.29, and Q(m) of 611. English WILEY Low-Temperature Sintering and Piezoelectric Properties of CuO-Added KNbO3 Ceramics Article 10.1111/jace.13225 1 JOURNAL OF THE AMERICAN CERAMIC SOCIETY, v.97, no.12, pp.3897 - 3903 JOURNAL OF THE AMERICAN CERAMIC SOCIETY 97 12 3897 3903 N scie scopus 000346099800029 2-s2.0-84915798649 Materials Science, Ceramics Materials Science Article (K0.5NA0.5)NBO3 CERAMICS MICROSTRUCTURE