Quoc Khanh Dang Henkensmeier, Dirk Krishnan, N. Nambi Jang, Jong Hyun Kim, Hyoung-Juhn Nam, Suk Woo Lim, Tae-Hoon 2024-01-20T09:33:57Z 2024-01-20T09:33:57Z 2021-09-05 2014-06 0376-7388 https://pubs.kist.re.kr/handle/201004/126738 Nation membranes with a monolayer of pores on one surface (P-Nation) were prepared by casting a Nation SE20092 dispersion containing ortho-dichlorobenzene. The pores are not connected but provide 2 mu m large openings, increasing the membrane surface by one dimension. The thickness of the porous layer is typically < 5 mu m. In catalyst coated membranes the catalyst layer penetrated the pores well The effect on the performance of a polymer electrolyte fuel cell (PEFC) was investigated at 95 degrees C. The porous layer formed the cathode, to enhance water back diffusion. After 24 h equilibration, 30-35 mu m thick P-Nafion gave 10-16% higher current density, reaching 858 mA/cm(2) at 0.4 V and 50% rh. N211 and P-Nafion equilibrated for 8 min showed peak power densities of 56 and 208 mW/cm(2) under anhydrous conditions, respectively, indicating that drying processes are slowed down. The stability of a MEA was tested for 240 h at 0.4 V and 50% rh (anode/cathode), without observable degradation. Under fully humidified conditions, the electrochemical surface area (ECSA) increased 40% in comparison to a N211 based MEA. At 65 degrees C, the ECSA more than doubled, showing 141 m(2)/g Pt. Also influence of the pores on water transport through a membrane and stability against membrane electrode delamination were considered. (C) 2014 Elsevier B.V. All rights reserved, English Elsevier BV Nafion membranes with a porous surface Article 10.1016/j.memsci.2014.03.003 1 Journal of Membrane Science, v.460, pp.199 - 205 Journal of Membrane Science 460 199 205 N scie scopus 000334287900020 2-s2.0-84896529465 Engineering, Chemical Polymer Science Engineering Polymer Science Article METHANOL FUEL-CELL WATER-UPTAKE PERFORMANCE DMFC TRANSPORT STACK Nafion membranes Porous surfaces Hierarchical structures Water management Fuel cells