Permana, Antonius Dimas Chandra Nugroho, Agung Chung, Kyung Yoon Chang, Wonyoung Kim, Jaehoon 2024-01-20T10:02:08Z 2024-01-20T10:02:08Z 2021-09-04 2014-04-01 1385-8947 https://pubs.kist.re.kr/handle/201004/126896 Hierarchically porous anatase titanium oxide (TiO2) microspheres were synthesized using a green supercritical methanol route over a very short reaction time of 15 min without using templates or surfactants. Primary nano-sized particles with diameters of 20-55 nm with organic coverage on the surface were loosely aggregated and formed secondary micron-sized particles 1.0-2.5 mu m in diameter, creating a porous structure with average pores 9-15 nm in diameter. When the as-synthesized microspheres were calcined under a Ar/5% H-2 condition, carbonization of the organic groups formed an ultrathin and uniform carbon layer on the nano-sized primary particles with a thickness of 0.5-1 nm and reduced some of the Ti4+ to Ti3+. Both the hierarchically porous structure and the conductive layer coating had positive effects by increasing Li ion storage capacity. The prepared TiO2 microspheres exhibited a high reversible discharge capacity of 212.3 mA h g(-1) at 0.1 C, a high-rate performance of 77.9 mA h g(-1) at 8 C, and an excellent capacity retention of >97% at the end of 100 cycles at 1.0 C, whereas TiO2 nanoparticles without porous structure and surface modification exhibited lower discharge capacities of 161.8 mA h g(-1) at 0.1 C and 5.2 mA h g(-1) at 8 C, and poorer capacity retention of 26%. The considerable improvement in the electrochemical performance was attributed to the nano-sized TiO2 primary particles, porous structure, and carbon coating and Ti3+ incorporation. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved. English ELSEVIER SCIENCE SA LI-ION BATTERIES CONTINUOUS HYDROTHERMAL SYNTHESIS METAL-OXIDE NANOPARTICLES HIGH-RATE PERFORMANCE PROMOTED H-DONATION SUPERCRITICAL WATER LITHIUM-STORAGE NANOSTRUCTURED MATERIALS SOLVOTHERMAL SYNTHESIS MESOPOROUS ANATASE Template-free synthesis of hierarchical porous anatase TiO2 microspheres with carbon coating and their electrochemical properties Article 10.1016/j.cej.2013.12.029 1 CHEMICAL ENGINEERING JOURNAL, v.241, pp.216 - 227 CHEMICAL ENGINEERING JOURNAL 241 216 227 scie scopus 000333720000025 2-s2.0-84891753378 Engineering, Environmental Engineering, Chemical Engineering Article LI-ION BATTERIES CONTINUOUS HYDROTHERMAL SYNTHESIS METAL-OXIDE NANOPARTICLES HIGH-RATE PERFORMANCE PROMOTED H-DONATION SUPERCRITICAL WATER LITHIUM-STORAGE NANOSTRUCTURED MATERIALS SOLVOTHERMAL SYNTHESIS MESOPOROUS ANATASE Titanium oxide Supercritical alcohol Carbon coating Porous Lithium-ion batteries