최선희 손지원 김우식 이종호 김주선 Sungmoon Kim 2024-01-21T03:04:48Z 2024-01-21T03:04:48Z 2021-09-06 2006-05 1229-7801 https://pubs.kist.re.kr/handle/201004/135534 We have deposited NiO films by RF sputtering on Al2O3/SiO2/Si and 100 nm-thick gadolianaGd doped CeO2 covered Al2O3/SiO2/Si substrates at various Ar/O2 ratios. The deposited films were reduced to form porous Ni thin films in 4 % H2 at 400℃. For the films deposited in pure Ar, the reduction was retarded due to the thickness and the orientation of the NiO films. On the other hand, the films deposited in oxygen mixed ambient were reduced and formed porous Ni films after 20 min of reduction. We also investigated the possibility of using the films for the single chamber operation by studying the electrical property of the films in the fuel/air mixed environment. It is shown that the resistance of the Ni film increases quickly in the mixed gas environment and thus further improvements of Ni-base anodes are required thought to be needed for using them in the single chamber operation. 한국세라믹학회 Fabrication and Properties of Porous Ni Thin Films Article 2 한국세라믹학회지, v.43, no.5, pp.1 - 1 한국세라믹학회지 43 5 1 1 kci ART001010435 Sputtering NiO Porous film Fuel cell anode Reduction1. Introduction Sputtering NiO Porous film Fuel cell anode Reduction1. Introduction