Kang, BH Joo, GT 2024-01-21T03:35:17Z 2024-01-21T03:35:17Z 2021-09-02 2006-03 0021-4922 https://pubs.kist.re.kr/handle/201004/135709 SrxBa1-xNb2O6 (SBN) ceramics were synthesized from Sr0.45Ba0.55Nb2O6 (45SBN) to 75SBN according to x content, and the mineral phases of ceramics were identified by XRD. Some SBN single crystals were grown by Czochralski method. There was only one single phase in from 45SBN to 70SBN when synthesizing at 1350 degrees C, but 75SBN ceramics had SrNb2O6 as second phase. The single crystal growth of SBN was generally difficult because of including bubbles, being black or poly-crystalline. This is considered to be related the properties of SBN ceramics synthesis as well as SBN melt. 60SBN and 75SBN single crystals have been grown in phi 4 cm Pt crucible with Pt wires as seed. And the crystals have grown to c-axis direction, and had some facets, which were identified. English INST PURE APPLIED PHYSICS RANDOM-FIELDS Dielectric properties of SrxBa1-xNb2O6 ceramics and single crystals Article 10.1143/JJAP.45.L245 1 JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, v.45, no.8-11, pp.L245 - L246 JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS 45 8-11 L245 L246 scie scopus 000236562200010 2-s2.0-33645969274 Physics, Applied Physics Article RANDOM-FIELDS SrxBa1-xNb2O6 (SBN) relaxor ferroelectrics Curie temperature diffusive phase transition Czochralski method single crystals