Jeun, MH Lee, KI Lee, WY Chang, JY Han, SH 2024-01-21T05:01:26Z 2024-01-21T05:01:26Z 2021-09-03 2005-06 0374-4884 https://pubs.kist.re.kr/handle/201004/136425 The magnetotransport properties of electroplated and sputtered Bi thin films have been investigated in the range 4-300 K. A marked increase from 5,200% to 80,000% in the ordinary magnetoresistance (MR) for the electroplated Bi thin film was observed after thermal anneal at 4 K. The MR ratios for the as-grown and the annealed Bi thin films were found to be 560% and 590%, respectively, at 300 K. On the other hand, the MR for the Bi film grown by sputtering was hardly observed at 4 and 300 K, whereas the MR ratios after annealing were found to reach 30,000% at 4 K and 600% at 300 K. The room temperature MR in the sputtered films was found to depend on the trigonal-axis oriented microstructures and grain size, in contrast to the electroplated films. Our results support the view that the grain-boundary scattering mechanism is dominant in the MR response at room temperature, whereas the textured grains oriented to the trigonal axis are dominant in the MR response at 4 K for both electroplated and sputtered samples. English KOREAN PHYSICAL SOC Magnetoresistance in semimetallic bismuth thin films Article 1 JOURNAL OF THE KOREAN PHYSICAL SOCIETY, v.46, pp.S80 - S82 JOURNAL OF THE KOREAN PHYSICAL SOCIETY 46 S80 S82 scie scopus kci ART000960583 000229589900019 2-s2.0-20444452550 Physics, Multidisciplinary Physics Article; Proceedings Paper semimetal bismuth magnetotransport ordinary magnetoresistance