Chang, JY Shan, A 2024-01-21T08:39:04Z 2024-01-21T08:39:04Z 2021-09-03 2003-06-15 0022-2461 https://pubs.kist.re.kr/handle/201004/138465 Intermediate heat treatment was employed to anneal pure Al samples subjected to cyclic Equal Channel Angular (ECA) pressing in order to investigate the microstructural change and tensile properties of as-pressed and annealed samples. As-pressed samples were annealed at 200 degreesC for 1 hr after 2 and 4 passages. Some annealed samples were pressed further to compare the changes in the properties of pure Al with the same equivalent strain induced by cyclic ECAP but having different thermal history. Intermediate annealing in the cyclic repetitive ECA pressing appears to be an effective method to form an equiaxed, fine-grained structure with high misorientation angle. It decreases the aspect ratio of subgrains while keeping the grains size unchanged. Annealing followed by further pressing results in an increase in the aspect ratio but small decrease in the grain size. It is speculated that recrystallization of ECA pressed aluminum is responsible for the significant increase in the misorientation angle. (C) 2003 Kluwer Academic Publishers. English KLUWER ACADEMIC PUBL SUBMICROMETER GRAIN-SIZE AL-MG ALLOY MICROSTRUCTURE DEFORMATION Intermediate annealing of pure aluminum during cyclic equal channel angular pressings Article 10.1023/A:1024426400723 1 JOURNAL OF MATERIALS SCIENCE, v.38, no.12, pp.2613 - 2617 JOURNAL OF MATERIALS SCIENCE 38 12 2613 2617 scie scopus 000183703800008 2-s2.0-0042807609 Materials Science, Multidisciplinary Materials Science Article SUBMICROMETER GRAIN-SIZE AL-MG ALLOY MICROSTRUCTURE DEFORMATION intermediate annealing equal channel angular pressing subgrain