이무성 정민진 김영필 김진봉 진문영 박민 2024-01-21T08:42:08Z 2024-01-21T08:42:08Z 2021-09-06 2003-06 1225-1089 https://pubs.kist.re.kr/handle/201004/138522 The effect of the length of fluoroalkyl substituents on the refractive index (n) and glass transition temperature (Tg) of methyl methacrylate (MMA)-fluoroalkyl methacrylate (FAMA) copolymers (poly(MMA/FAMA)) was investigated. The copolymers were solution-polymerised in order to prepare cladding materials for plastic optical fiber (POF). The copolymer composition, Tg, and refractive index (n) of the copolymers were determined using 1H-NMR spectroscopy, differential scanning calorimeter, and prism coupler, respectively. As the length of fluoroalkyl units in FAMA and the content of FAMA in poly (MMA/FAMA) increased, the Tg and n decreased monotonically. This indicates that although the copolymerization of MMA and FAMA is effective in controlling the n of cladding materials, the decrease in Tg is inevitable. The interfacial instability between PMMA and MMA-trifluoroethyl methacrylate (TFEMA) copolymers, observed during annealing at 170oC, was greater at higher TFEMA contents. The observation was interpreted in terms of the solubility parameter concept combined with the Flory-Huggins interaction parameter. 한국섬유공학회 고내열 POF용 클래딩 재료 제조(I) -Methyl Methacrylate/Fluoroalkyl Methacrylate 공중합체- Preparation of Cladding Polymers for Heat Resistant Plastic Optical Fiber(I) -Methyl Methacrylate/Fluoroalkyl Methacrylate Copolymers- Article 2 한국섬유공학회지, v.40, no.4, pp.335 - 340 한국섬유공학회지 40 4 335 340 kci ART000938669 plastic optical fiber cladding polymer random copolymer fluoroalkyl methacrylate plastic optical fiber cladding polymer random copolymer fluoroalkyl methacrylate