Lyoo, WS Han, SS Kim, JH Yoon, WS Lee, CJ Kwon, IC Lee, J Ji, BC Han, MH 2024-01-21T14:46:30Z 2024-01-21T14:46:30Z 2021-09-05 1999-11 0003-3146 https://pubs.kist.re.kr/handle/201004/141862 Vinyl pivalate (VPi) was bulk-polymerized at 30, 40, and 50 degrees C using a low temperature initiator, i.e. 2,2'-azobis(2,4-dimethylvaleronitrile) (ADMVN). The effects of polymerization temperature and initiator concentration were investigated in terms of polymerization behavior and molecular structures of poly(vinyl pivalate) (PVPi) and corresponding poly(vinyl alcohol) (PVB) microfibrillar fiber obtained by saponification in KOH/methanol/water, Low polymerization temperature using ADMVN proved to be successful in obtaining PVA of syndiotacticity-rich high molecular weight. PVPi had a number-average degree of polymerization (P-n) of 27 100-35 900, and a degree of branching for pivaloyl group of 0.8-1.0 at 30 degrees C, 1.0-1.3 at 40 degrees C, and 1.4-1.7 at 50 degrees C at conversions below 40%. Saponification of PVPi yielded PVA having a P-n of 10 400-16 500, and syndiotactic diad (S-diad) content of 58.8-61.5%. It was found that all PVA specimens represented microfibrillar morphologies, with high crystallinity and orientation. The S-diad content and crystal melting temperature were higher with PVA prepared from PVPi polymerized at lower temperatures. English WILEY-V C H VERLAG GMBH SUSPENSION POLYMERIZATION ACETATE POLYVINYLALCOHOL Bulk polymerization of vinyl pivalate using low-temperature azoinitiator and saponification for the preparation of poly(vinyl alcohol) microfibrils Article 1 ANGEWANDTE MAKROMOLEKULARE CHEMIE, v.271, pp.46 - 52 ANGEWANDTE MAKROMOLEKULARE CHEMIE 271 46 52 scie scopus 000084409100009 2-s2.0-0002024758 Polymer Science Polymer Science Article SUSPENSION POLYMERIZATION ACETATE POLYVINYLALCOHOL