Kim, JK Yu, JW Cho, HN Kim, DY Kim, CY 2024-01-21T16:11:55Z 2024-01-21T16:11:55Z 2021-09-03 1999-01 1058-725X https://pubs.kist.re.kr/handle/201004/142613 Poly(9,9'-di-n-hexyl-2,7-fluorenylenevinylene) (PDHFV) was synthesized with dibromodihexylfluorene and divinyldihexylfluorene by employing a Heck reaction with a palladium catalyst. The UV-visibIe absorption maximum at 400 nm from the polymer solution in chloroform has redshifted by 40 nm for the polymer film. The photoluminescence (PL) spectrum of the film showed the emission maximum at 470 nm with a strong excimer emission at 535 nm. The ratio of the excimer emission intensity to that of the singlet decay was constant regardless of the excitation energy However, the indirect excitation of the fluorophore for the PL emission of a polymer blend at 470 nm was greatly enhanced at the expense of the excimer emission intensity. English GORDON BREACH SCI PUBL LTD Effective exciton confinement in a light emissive polymer Article 10.1080/10587259908026805 1 MOLECULAR CRYSTALS AND LIQUID CRYSTALS SCIENCE AND TECHNOLOGY SECTION A-MOLECULAR CRYSTALS AND LIQUID CRYSTALS, v.327, pp.165 - 170 MOLECULAR CRYSTALS AND LIQUID CRYSTALS SCIENCE AND TECHNOLOGY SECTION A-MOLECULAR CRYSTALS AND LIQUID CRYSTALS 327 165 170 N scie scopus 000082384500040 2-s2.0-0041725714 Crystallography Crystallography Article; Proceedings Paper CONJUGATED POLYMERS EMITTING-DIODES BLUE light-emissive polymer exciton excimer energy transfer polymer blend