Kang, Y.S. Jung, B. Park, H.C. Won, J. Kim, U.Y. Kim, J. Rhee, H.-W. 2024-01-21T18:07:15Z 2024-01-21T18:07:15Z 2021-09-02 1997-09 1225-5947 https://pubs.kist.re.kr/handle/201004/143638 An integrally skinned asymmetric polysulfone membrane was prepared by the phase inversion method. Its skin was defect-free so that an additional coating process was not necessary to caulk the skin defects for gas separation. Its separation factor of oxygen over nitrogen reached 5. Such a high separation factor could arise from the gelation of the interfacial layer between the dope solution and the gelation medium due to its increased polymer concentration before the liquid-liquid demixing. Experimentally, the polymer concentration at interface was controlled by the flux ratio of solvent to nonsolvent. R. which was, in turn, manipulated by introducing a cosolvent, ethyl acetate. Because the cosolvent has lower surface tension than the main solvent, N-methyl pyrrolidinone, the cosolvent-rich layer might be formed at the interface, which seemed to primarily control the flux ratio of solvent to nonsolvent. It was verified that an integrally skinned membrane without skin defects could be formed when the polymer concentration at interface was high before the onset of liquid-liquid demixing, and that the flux ratio played a crucial role in determining the membrane morphology. English Formation of integrally skinned asymmetric membranes without skin defects for gas separation Article 1 Korea Polymer Journal, v.5, no.3, pp.166 - 172 Korea Polymer Journal 5 3 166 172 scopus 2-s2.0-0000552480 Article gas separation ntegrally skinned asymmetric membrane membrane formation