Byun, J.-O. Kim, B.-H. Hong, K.-S. Jung, H.-J. Lee, S.-W. Izyneev, A.A. 2024-01-21T21:12:30Z 2024-01-21T21:12:30Z 2022-01-10 1995-01 0022-3093 https://pubs.kist.re.kr/handle/201004/145389 The properties and structure of (45 - x)RO · xNa2O · 2.5Al2O3 · 52.5P2O5 (R = Mg, Ca, Sr, Ba, 0 ≤ x ≤ 31 mol%) glasses were investigated. The variation in the molar volumes of glasses in the MgO series is closely related to the formation of the end groups in the glasses with the substitution of Na+ ions for Mg2+ ions, resulting in a variation of the density and refractive index of the glasses. The properties of glasses containing CaO in terms of Na2O substitution depend mainly on the low field strength of Na+ ions substituting for CaO even though the end groups occurring in the glasses increased. The variation in properties of the glasses containing SrO and BaO, some of which were substituted by Na2O, could be explained by differences in masses, field strength and polarizability between the Na+ ions and the alkaline-earth ions due to a small variation in the structure of the glasses despite Na2O substitution. ？ 1995. English Properties and structure of RONa2OAl2O3P2O5 (R = Mg, Ca, Sr, Ba) glasses Article 10.1016/0022-3093(95)00280-4 1 Journal of Non-Crystalline Solids, v.190, no.3, pp.288 - 295 Journal of Non-Crystalline Solids 190 3 288 295 scopus 2-s2.0-34547309312 Article