CHOI, JO LEE, JJ HAN, SH KIM, HJ KANG, IK 2024-01-21T21:37:17Z 2024-01-21T21:37:17Z 2021-09-02 1994-05-15 0021-8979 https://pubs.kist.re.kr/handle/201004/145577 Fe-Hf-C-N films with excellent soft magnetic properties were fabricated by Ar+N2 reactive sputtering for the first time. The newly developed films were found to have better soft magnetic properties than those of Fe-Hf-C or Fe-Hf-N films. The best magnetic properties achieved in this work are H(c) of 0.15 Oe, mu(eff) of 8200, and 4 piM(s) of 17 kG. The thermal stability of the Fe-Hf-C-N films was also found to be excellent, e.g., H(c) was less than 0.3 Oe and mu(eff) was about 4000 for the films annealed up to 700-degrees-C. It was observed by transmission electron microscopy that the films consisted of two phases: a fine crystalline a-Fe phase whose grain size is about 6 nm, and Hf(C,N) precipitates with a size of less than 2 nm. The fine grained alpha-Fe structures, together with finely dispersed Hf(C,N) precipitates, is considered to be one of the main factors for the excellent magnetic properties and thermal stability. English AMER INST PHYSICS SOFT-MAGNETIC PROPERTIES OF NANOCRYSTALLINE FE-HF-C-N FILMS Article 10.1063/1.355562 1 JOURNAL OF APPLIED PHYSICS, v.75, no.10, pp.5785 - 5787 JOURNAL OF APPLIED PHYSICS 75 10 5785 5787 scie scopus A1994NN73400114 2-s2.0-0345252539 Physics, Applied Physics Article; Proceedings Paper Fe alloy