PARK, JG OH, TS KIM, YH 2024-01-21T23:04:30Z 2024-01-21T23:04:30Z 2021-09-02 1992-11-01 0022-2461 https://pubs.kist.re.kr/handle/201004/146354 Dielectric properties and microstructural behaviour of Ba1-xSrxTi1-yCayO3-y ceramics, where strontium and calcium were doped on the barium and titanium sites, respectively, within the range 0 less-than-or-equal-to x less-than-or-equal-to 0.24 and 0 less-than-equal-to y less-than-or-equal-to 0.05, were investigated. Calcium addition decreased the tetragonality, c/a, increased the unit cell volume, and lowered the Curie temperature, which were all attributed to the occupancy of Ca2+ ions on titanium sites. When sintered at a low oxygen partial pressure of 10(-9) MPa, a resistivity higher than 10(11) OMEGA cm was maintained for the formulations containing B-site calcium substitution more than 0.5 mol %. With increasing the amount of calcium addition, the Curie peak was depressed and completely broadened for the compositions with calcium addition more than 3 mol %, where the average grain size was smaller than 1 mum. Co-firing with nickel electrodes in a reducing atmosphere also depressed the Curie peak and inhibited the grain growth due to the diffusion of nickel into the dielectrics. English CHAPMAN HALL LTD BATIO3 DIELECTRIC-PROPERTIES AND MICROSTRUCTURAL BEHAVIOR OF B-SITE CALCIUM-DOPED BARIUM-TITANATE CERAMICS Article 10.1007/BF01119727 1 JOURNAL OF MATERIALS SCIENCE, v.27, no.21, pp.5713 - 5719 JOURNAL OF MATERIALS SCIENCE 27 21 5713 5719 scie scopus A1992JW11900005 2-s2.0-0347119584 Materials Science, Multidisciplinary Materials Science Article BATIO3 barium titanate B-site Ca doping reduction inhibition microstructure