LEE, KR YOON, DN 2024-01-21T23:12:38Z 2024-01-21T23:12:38Z 2022-01-11 1992-01 0956-7151 https://pubs.kist.re.kr/handle/201004/146488 When a 90Mo-10Ni alloy (by wt) liquid phase sintered at 1400-degrees-C is heat-treated at 1400-degrees-C after replacing the matrix with a melt of 44Ni-34Mo-22W (by wt), the liquid films between the grains migrate, leaving behind an Mo alloy enriched with W. The ratio of the lattice diffusivity of W in Mo, D, to the initial migration velocity, upsilon, (D/upsilon) is estimated to be between 0.03 and 0.18 angstrom. Hence, it appears that there is no lattice diffusion of W ahead of the migrating liquid film, and in such a case the driving force has been suggested to be the chemical free energy. But the observed v is approximately same as that to be expected if the driving force is assumed to be diffusional coherency strain energy. Likewise, a previous study of den Broeder and Nakahara shows that the rate of chemically-induced grain boundary migration in Cu-Ni shows a smooth variation with temperature as D/upsilon decreases from values much larger than the interatomic spacing to values much smaller with decreasing temperature. The coherency strain energy thus appears to be a general driving force for the migration even when the apparent diffusion length indicated by D/upsilon is smaller than the interatomic spacing. English PERGAMON-ELSEVIER SCIENCE LTD GRAIN-BOUNDARY MIGRATION COHERENCY STRAIN NI SYSTEM ALLOY CHEMICALLY-INDUCED LIQUID-FILM MIGRATION WITH LOW LATTICE DIFFUSIVITY RELATIVE TO THE MIGRATION RATE IN MO-NI-(W) Article 10.1016/0956-7151(92)90203-Q 1 ACTA METALLURGICA ET MATERIALIA, v.40, no.1, pp.107 - 111 ACTA METALLURGICA ET MATERIALIA 40 1 107 111 scie scopus A1992GV80400009 Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering Materials Science Metallurgy & Metallurgical Engineering Article GRAIN-BOUNDARY MIGRATION COHERENCY STRAIN NI SYSTEM ALLOY