Dharmaiah, Peyala Park, Gwang Min Heo, Minsu Ju, Jaebaek Kim, Hyun-Sik Park, Hea Jung Won, Sung Ok Kim, Tae Heon Kim, Seong Keun Kim, Jin-Sang Baek, Seung-Hyub 2025-10-01T11:02:28Z 2025-10-01T11:02:28Z 2025-09-30 2025-09 0925-8388 https://pubs.kist.re.kr/handle/201004/153304 Two-dimensional (2D) layered Zintl compounds have emerged as promising candidates for thermoelectric applications due to their favorable electronic structures, efficient charge transport pathways, and loosely bound cations. In this study, we engineered 2D-layered structures in polycrystalline ZnSb through alkali metal (A = Li, Na, K) alloying, inducing a bonding transition from sp(3) to sp(2) hybridization that promotes the formation of layered structures. Structural analysis confirmed the formation of layered phases, with increasing texturing fractions from Li to K. Electrical transport measurements revealed that LiZnSb exhibited high electrical conductivity (similar to 6561 S cm(-1)) due to a high carrier concentration, while NaZnSb showed moderate conductivity (similar to 213 S cm(-1)) with a carrier concentration close to the theoretical value (7.38 x10(18) cm(-3)). In contrast, KZnSb demonstrated extremely low conductivity, hindering reliable carrier concentration analysis. As a result, NaZnSb achieved a maximum ZT of 0.079 at 375 K, which is significantly higher than that of LiZnSb. The single parabolic band (SPB) model suggests that NaZnSb may be further optimized through extrinsic doping at the Zn site, whereas LiZnSb remains limited by intrinsic cation deficiencies. These results demonstrate that alkali metalinduced bonding transitions offer a viable strategy for engineering 2D structures in Zintl compounds to enhance thermoelectric performance. English Elsevier BV Development of two-dimensional layered ZnSb-based thermoelectric materials via alkali metal alloying Article 10.1016/j.jallcom.2025.183309 1 Journal of Alloys and Compounds, v.1039 Journal of Alloys and Compounds 1039 N scie scopus 001567928700001 2-s2.0-105014512294 Chemistry, Physical Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering Chemistry Materials Science Metallurgy & Metallurgical Engineering Article OXIDES Thermoelectric materials Zintl phase Alkali metal Carrier concentration optimization Lattice thermal conductivity