Modification of the interface in SiC/Al composites

Authors
Lee, JCAhn, JPShi, ZKim, YLee, HI
Issue Date
2000-09
Publisher
MINERALS METALS MATERIALS SOC
Citation
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, v.31, no.9, pp.2361 - 2368
Abstract
Methodologies both to avoid the formation of Al4C3 and to tailor the interfacial structures in a SiC/2014 Al composite were demonstrated. Modification of the interfacial structures in the SiC/2014 Al composite was made by forming SiO2 layers on the surfaces of SIC via passive oxidation at elevated temperatures. In the 2014 Al composite reinforced with the oxidized SiC, MgAl2O4 and Si crystals were observed to be present at the interfacial region as a result of the reaction between the SiO2 layer and the matrix. On the other hand, in the case of the 2014 Al composite reinforced with unoxidized SiC, SiC was found to react with the Al matrix to form both Al4C3 and Si. Qualitative measurements of the interfacial bonding strength were carried out on composites having various types of interfaces and thicknesses. Detailed interfacial structures and phase identifications, which were examined using scanning electron microscopy (SEM) and transmission electron microscopy (TEM), were presented.
Keywords
METAL-MATRIX COMPOSITES; SILICON-CARBIDE; SI CONTENTS; ALUMINUM; OXIDATION; FABRICATION; PREDICTION; PARTICLES; SUPPRESS; AL4C3; METAL-MATRIX COMPOSITES; SILICON-CARBIDE; SI CONTENTS; ALUMINUM; OXIDATION; FABRICATION; PREDICTION; PARTICLES; SUPPRESS; AL4C3; Al composite; interface modification; SiC oxidation; HRTEM
ISSN
1073-5623
URI
https://pubs.kist.re.kr/handle/201004/141136
DOI
10.1007/s11661-000-0151-x
Appears in Collections:
KIST Article > 2000
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML

qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE