Fibroblast culture on poly(L-lactide-co-ε-caprolactone) an electrospun nanofiber sheet

Title
Fibroblast culture on poly(L-lactide-co-ε-caprolactone) an electrospun nanofiber sheet
Authors
장봉석정영미권일근문초혜김수현
Keywords
electrospinning; PLCL; fibroblast cells; cell matrix engineering
Issue Date
2012-12
Publisher
Macromolecular research
Citation
VOL 20, NO 12, 1234-1242
Abstract
Electrospinning has been used to make a nanofibrous matrix for vascular tissue engineering applications. The poly(L-lactide-co-ɛ-caprolactone) (PLCL) copolymer (50:50), which is biodegradable and elastic, was used to fabricate electrospun nanofiber sheets with a thickness of 20–50 μm. The objective of this study was to investigate the behavior of fibroblast cells on the PLCL electrospun sheet. The cell proliferation on the PLCL electrospun sheet was evaluated. The cell morphology was observed using scanning electron microscopy. Several coating materials were evaluated to increase cell adhesion, including fibronectin, Type-I collagen, and gelatin. Among the coating materials tested, Type-I collagen gave the best result. Cell proliferation at all cell densities was tested steadily increase up to 3 weeks. Single side cell seeding and double side cell seeding were compared. During cell proliferation for 3 and 7 days, the single side cell seeding slowly increased, whereas rapid cell growth was observed for the double side seeding. We evaluated the mechanical properties of electrospun nanofiber scaffolds cultured with different cell volumes. In these experiments, a higher cell volume resulted in higher tensile strength and Young’s modulus. Further studies are being conducted to design a functional tubular vascular scaffold with adequate mechanical properties and architecture to promote cell growth.
URI
https://pubs.kist.re.kr/handle/201004/44297
ISSN
15985032
Appears in Collections:
KIST Publication > Article
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE