XANES and DRIFTS study of sulfated Sb/V/Ce/TiO2 catalysts for NH3-SCR
- XANES and DRIFTS study of sulfated Sb/V/Ce/TiO2 catalysts for NH3-SCR
- Pullur Anil Kumar; 정영은; Sanjeev Gautam; 하헌필; 이경주; 채근화
- XANES; NOx conversion; DRIFTS; Ce(III) sulfate species; Ce edge
- Issue Date
- Chemical engineering journal
- VOL 275, 142-151
- A study of structural and mechanistic investigation of the Sb/V/Ce/Ti catalysts sulfated at different temperatures was carried out by X-ray absorption near edge spectroscopy (XANES) and diffused reflectance infrared Fourier transformed spectroscopy (DRIFTS). The high temperature sulfated catalyst, especially Sb/V/Ce/Ti-S500 (sulfated at 500 °C temperatures), exhibited superior NOx conversion at low temperatures (150–200 °C) compared to Sb/V/Ce/Ti-S400 and Sb/V/Ce/Ti-S300 (sulfated at 400 and 300 °C) catalysts. The Ce L3 edge XANES spectra of Sb/V/Ce/Ti-S500 catalyst showed the formation of Ce(III) dominant sulfate species, resulting in the enhancement of Lewis and Brønsted acid strength. The formation of Ce(III) sulfate species on Sb/V/Ce/Ti-S500 catalyst was clearly indicated by Ce M4,5 and S K edge XANES spectra peaks at 881.9 eV attributed to Ce3+ oxidation state and 2481 eV assigned to S6+ oxidation state of sulfate species. Furthermore, the in situ DRIFTS results revealed that the Lewis and Brønsted acid sites of Sb/V/Ce/Ti-S500 catalysts increased significantly, followed by Sb/V/Ce/Ti-S400 and Sb/V/Ce/Ti-S300. At 200 °C, the reaction between the pre-adsorbed NH3 species with NO + O2 on sulfated catalysts exhibited the formation of mono-dentate, bi-dentate, bridging nitrates and NO2 species. Meanwhile, the subsequent formation of NO2 via NO oxidation was promoted on Sb/V/Ce/Ti-S400 and Sb/V/Ce/Ti-S500 catalysts, followed by surface interaction with adsorbed NH3 to produce N2 and H2O at low temperatures (<220 °C).
- Appears in Collections:
- KIST Publication > Article
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.