Unraveling the Atomistic Sodiation Mechanism of Black Phosphorus for Sodium Ion Batteries by First-Principles Calculations

Abstract

As opposed to the standard graphite anode used for lithium (Li) ion batteries (LIBs), a standard anode material for sodium (Na) ion batteries (NIBs) has not yet been reported. Black phosphorus is potentially very attractive as an anode material for NIBs, as it has a layered structure similar to graphite but a greater interlayer distance. In this work, we propose an atomistic mechanism for the sodiation of black phosphorus, based on first-principles calculations. The layered structure of black phosphorus is maintained up to the composition of Na0.25P, with one-dimensional sodiation (an intercalation process) occurring in the interlayer spaces of the black phosphorus, resulting in sliding of the phosphorene layers because one Na atom tends to bind to four P atoms. At Na levels beyond Na0.25P, the intercalation process changes to an alloying process. Sodiation exceeding the critical composition leads to breaking of P-P bonds and eventual formation of an amorphous phase from the layered NaxP structure. After the P-P bonds in the layered NaxP structure are progress in which staggered P-P bonds are preferentially broken rather than planar P-P bonds, P-2 dumbbells are generated. As sodiation proceeds further, most of the P-2 dumbbells become isolated P atoms. Thus, in the amorphous Na3P phase, only low-coordinate P components such as isolated atoms (primarily) and dumbbells are found. We expect that our comprehensive understanding of the sodiation mechanism in black phosphorus will provide helpful guidelines in designing new types of black phosphorus anodes to obtain better performing NIBs.